Product description 产品描述
This kind of products is applicable for 10KV cross-linkable semi-conductive shielding between conductors of extrusion insulation power cables and insulation layers. It is manufactured with domestic raw materials by Swiss BUSS extrusion equipment through compounding process. It has excellent mechanical properties and stable processability.
本产品适用于10KV挤包绝缘电力电缆导体与绝缘层交联型半导电屏蔽，采用国内原辅助材料经先进的瑞士BUSS设备混炼加工而成，具有优良机械性能和加工稳定性。
 
Processing Indicator 加工工艺
Recommend to process with the PE extruder. 建议使用聚乙烯专用挤出机进行加工。

Model 牌号	Machine Barrel Temperature 机筒温度	Molding Temperature 机头温度
YPJ-10 / YPB-10	70-110℃	110-118℃

 
 
Physical and Electrical Properties 物理和电气性能

Item 试验项目	Unit 单位	Technical requirements 技术要求
		YPJ-10	YPB-10
Relative Density 相对密度	g/cm3	≤1.13	≤1.16
Tensile Strength 拉伸强度	MPa	≥12	≥10
Elongation at Break 断裂伸长率	%	≥180	≥200
20℃Volume Resisitivity 20℃体积电阻率	Ω·cm	≤100	≤100
Volume Resisitivity 体积电阻率90℃	Ω·cm	≤5000	≤2500
90℃Volume Resisitivity after air aging(100℃×168h)  100℃ 168小时空气热老化后 90℃时体积电阻率	Ω·cm	≤1000	≤500
Air Aging Test 空气热老化试验	(135±2℃)×168h
Tensile Strength Variation After Aging 拉伸强度变化率	%	±30	±30
Elongation Variation After Aging 断裂伸长变化率	%	±30	±30
Hot Set Test 热延伸	200℃×0.2MPa×15min
Hot Elongation 负荷下伸长率	%	≤100	≤100
Permanent Deformation after Cooling 冷却后永久变形(Set)	%	≤15	≤15
Peel Strength 剥离强度20℃	N/cm	----	10-45
Moisture Content 水分含量	ppm	≤900	≤900